310 s stainless steel plate has good resistance to high temperature, the temperature more than 800 [1], the began to soften, allowable stress begin to continue to reduce, the highest temperature 1200

310 s stainless steel plate has good resistance to high temperature, the temperature more than 800 [1], the began to soften, allowable stress begin to continue to reduce, the highest temperature 1200 ℃.Nickel (Ni), chromium (Cr) content is high, has good resistance to oxidation and corrosion resistance, acid and alkali resistance, high temperature performance, high temperature resistant steel pipe is dedicated to manufacturing occasions such as the electric heating furnace tubes, stainless steel after the increase of carbon content in austenite size, due to its solid solution strengthening effect strength was improved, the chemical composition of stainless steel austenite size features based on chromium, nickel, add, tungsten molybdenum, niobium and titanium elements, due to its organization is face-centered cubic structure, thus has high strength and creep at high temperature strength.

MMechanical properties:

Hardness (HB) : 187 or less

Tensile strength (б) b (Mpa) : p. 515

(10) sigma yield strength (Mpa) : more than or equal to 205 sigma

% is greater than or equal to 35

Area reduction % : no less than 50

1. Recommended heat treatment system: 1030 c -1180 c, quenching;

2. Mechanical properties include (1) tensile strength: not less than 520;(2) non-proportional extension strength: no less than 205;(3) elongation after fracture: not less than 35;

3. Density: 7.98